Casting is a common method in industrial manufacturing models where casting is relatively small and the internal stresses in the product are low. Therefore, the production investment is small, and large-scale parts with excellent performance can be obtained, but the production cycle is long, and mechanical processing is required after molding. At present, casting, casting, casting, Precision casting, rotary casting and centrifugal casting are derived. This article mainly describes the specific process flow of casting.
1. Before casting, you must be fully familiar with the process documentation of the castings. Before casting, you should know the casting sequence, the required molten steel material, the weight and the distribution of the mold. Check whether the number of ladle, repair quality and drying preheating are qualified, and whether the crane is running normally.
2. Check whether the sand box clamp and the lock box bolt are firm and firm, the weight of the pressure iron is appropriate, and whether the riser ring, the gate cup, the gate plug, etc. are properly installed. Eliminate the unsafe factors of the casting channel.
3. According to the casting sequence, the process requirements and the gate plugs required for the castings are properly placed. According to the casting sequence, the process requirements and the gate plugs required for the castings are properly placed.
4. Immediately after the start of casting, bleed air, while venting while casting, large castings should ignite the ignition material beside the hole. When casting large parts, after pouring, note one or two times from the riser, and the thin shell of the riser must be opened before pouring.
5. When the molten steel is poured to the height of the riser 1/3, it should be placed according to the quantity. Immediately after casting, the molten steel overflowing from the nozzle and the riser should be removed, and the pouring cup should be removed to facilitate the normal shrinkage of the falling sand and the casting.
6. After the molten steel is completely solidified, the mold can be moved. In the later stage of casting, pay attention to the amount of molten steel in the package. For the casting of important parts, the phenomenon of slag is not allowed to be poured, and the remaining molten steel is poured into the remaining tank (type).
7. The remaining sand type should be covered so that it can be re-arranged. If the sand type storage time does not exceed 48 hours, it can be cast normally. If it exceeds 48 hours, it should be checked to see if the mold meets the requirements. No casting.
For experienced casters, these processes are no longer familiar, but for beginners, the study of these processes is essential, and a good casting process can make castings more precise.